GETILAN ATP/130
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sLUmBk_GETILAN-ATP-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN is the trade-mark of our crosslinkable polythene. GETILAN ATP/130 GRAFTING is a high density chemically crosslinkable polythene to produce relatively flexible hoses suitable for hydro-thermosanitary features and also for potable water conduction. It is a conveniently grafted polythene able to react in presence of moisture and of catalyst. We normally suggest our type MAC/100 PSF. REACTION BETWEEN GRAFTING AND CATALYST: These two polythenes, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.50 - 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 24.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 370 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Service Temperature | -60 - 100 | °C |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Pressure Test | |||
| 95°C 1 | Pass | ||
| 95°C 2 | Pass |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 175 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C | |
| Die Temperature | 220 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90°C for two hours (up to 3 mm thickness). Steam treatment at 0.15 bar for 5/6 hours. |
| Note Message | |
|---|---|
| 1 . | 1 hr, 4.8 MPa |
| 2 . | 1000 hr, 4.4 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STRANOX C-PP15%LFT | Oxford Polymers | PP Copolymer | STRANOX |
| Sylvin 8215-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SUPREME GPPS SC 202EL | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| TAIRILAC AX4000 | Formosa Plastics Corporation | ABS | TAIRILAC |
| INSTRUC PCPBTGF30IM | Infinity LTL Engineered Compounds | PC+PBT | INSTRUC |