RTP 901 L
| Category: | PSU , Polysulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sKNHaH_RTP-901-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 | % | ASTM D955 |
| Moisture Content | 0.15 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 690 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 332 to 371 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Injection Pressure | 68.9 to 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ HC MT317 | PolyOne Corporation | TPE | Versaflex™ |
| Fainplast PVC CRKA 87 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LUVOCOM® 1106-7227 | Lehmann & Voss & Co. | PEI | LUVOCOM® |
| Petrothene® GA501026 | LyondellBasell Industries | LLDPE | Petrothene® |
| Rotuba CAB B902 (20% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |