Vyncolit® X620
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sIUXt7_Vyncolit-X620.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit X620 is a glass fibre and graphite filled phenolic moulding compound with low friction resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Apparent Density | 0.75 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.22 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 0.10 | % | ISO 62 |
| Post Shrinkage | 0.010 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.0 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Type | PF 2 C1 | ||
| Pourability | Good |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2 |
| Flexural Modulus | 15000 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Compressive Stress | 170 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 3.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 4.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 121-75M100 | ExxonMobil Chemical | TPV | Santoprene™ |
| Silmar® SIL90BA-585 | Interplastic Corporation | Polyester, TS | Silmar® |
| ELITE™ NG 5401B | The Dow Chemical Company | EPE | ELITE™ |
| Karina GRAY COLOR CONCENTRATE -E 18/ 89-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID A GV30 HYD2 RC black | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |