HiFill® PPSU GY061
| Category: | PPSU , Polyphenylsulfone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sHVr0C_HiFill-PPSU-GY061.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PPSU GY061 is a Polyphenylsulfone (PPSU) product. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 69.6 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 2450 | MPa | ASTM D790 |
| Flexural Strength | 88.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 207 | °C | ASTM D648 |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.57 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 160 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 357 to 391 | °C | |
| Middle Temperature | 357 to 391 | °C | |
| Front Temperature | 357 to 391 | °C | |
| Processing (Melt) Temp | 343 to 399 | °C | |
| Mold Temperature | 110 to 149 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7750 T GF 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| ExxonMobil™ HDPE HD 9830.02 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Edistir® RK 451G | Versalis S.p.A. | PS (HIPS) | Edistir® |
| Edgetek™ NY-20CF/000 BLACK | PolyOne Corporation | Nylon 6 | Edgetek™ |
| LNP™ LUBRILOY™ UA200A compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |