Hyundai EP Adhesives VE400S/1002
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP Adhesives |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sG8U9D_Hyundai-EP-Adhesives-VE400S-1002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hyundai EP Adhesives VE400S/1002 is an Ethylene Vinyl Acetate Copolymer (EVA) product. It is available in Asia Pacific. Applications of Hyundai EP Adhesives VE400S/1002 include adhesives/tapes and coating applications. Primary characteristic: good adhesion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.949 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 43 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 9.81 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 75.0 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion Strength | > 6.9 | kN/m | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STYRON A-TECH™ 1290 | Americas Styrenics LLC | PS (GPPS) | STYRON A-TECH™ |
| Caltex PP M710 | GS Caltex | PP Impact Copolymer | Caltex PP |
| Cheng Yu A700UV | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| Converge® Polyol 212-10 | Novomer, Inc. | PC | Converge® |
| Integra™ PC5025 F1 FR CL | PolySource, LLC | PC | Integra™ |