Alpha PVC 2212/7-118 CLEAR 0003
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | Alpha PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sG0n7S_Alpha-PVC-2212-7-118-CLEAR-0003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 2212/7-118 CLEAR 0003 is a PVC compound produced with FDA sanctioned raw materials. Crystal clear rigid parts can be produced with this formulation which features high flow and excellent heat stability for easy molding. 2212/7-118 CLEAR 0003 has become the standard in the medical industry for a variety of applications such as connectors, drip chambers and accessories to medical bags and catheters. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 - 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, 6.35 mm) | 76 - 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2040 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 1.91mm | 62.9 | MPa | ASTM D638 |
| Fracture, 1.91mm | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 1.91 mm) | 7.0 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 67.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 54.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 149 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 166 | °C | |
| Nozzle Temperature | 182 | °C | |
| Processing (Melt) Temp | 171 - 182 | °C |
| Injection instructions |
|---|
| Zone 4: 340°FZone 5: 350°F |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 166 | °C | |
| Cylinder Zone 4 Temp. | 171 | °C | |
| Cylinder Zone 5 Temp. | 177 | °C | |
| Adapter Temperature | 182 | °C | |
| Melt Temperature | 171 - 182 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 4720XWZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| NOVA ABS 770 NAT | NOVA Polymers, Inc. | ABS | NOVA ABS |
| China PPS hGR50 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| KOPLA PA66 KDG1133CR | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| LEXAN™ EXL9132 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |