Envir® PA66G33HL-BK0101
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Barnet |
| Trademark: | Envir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sFzCmM_Envir-PA66G33HL-BK0101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Envir® PA66G33HL-BK0101 is a 33% Glass fiber reinforced Nylon 66 molding resin, it is Heat stabilized and hydrolysis resistant. 66G33HL is optimized for properties and processibility. It is provided Black in color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Ash Content | 33 | % | ASTM D5630 |
| Moisture Content | < 0.20 | % | ASTM D6980 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Granularity | 3.50 | g/100 pellets |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9880 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 180 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 10300 | MPa | ISO 178 |
| Flexural Stress | 280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 11 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 260 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ H20QM21 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| Pyramid™ PEI II2150 | Polymics, Ltd. | PEI | Pyramid™ PEI |
| SILIMIX 59D2 | SILON s.ro | Siloxane, UHMW | SILIMIX |
| HIVOREX 5000S | Lotte Chemical Corporation | HDPE | HIVOREX |
| OTECH PVC OM5513-Soles | OTECH Corporation | PVC, Unspecified | OTECH PVC |