Durethan® C 38 FAM 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sFbIKG_DurethanC38FAM000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6-Copolymer, non-reinforced,Extrusion |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.13 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/2.16 kg) | 5.00 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 10 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ISO 62 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 212 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | -- | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | -- | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C, 1 MHz) | -- | 3.00 | IEC 60250 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/IPDI,ES, 18-020 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEC-365 | SHIN-A T&C | Epoxy | SHIN-A |
| Starex GR-4020L | SAMSUNG SDI CO., LTD. | ABS | Starex |
| NEFTEKHIM PP 8400K | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Ferro PP LPP10YE08NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| POLIMAXX MH-1 | IRPC Public Company Limited | ABS | POLIMAXX |