Order Products : sales@su-jiao.com
ATTANE™ 4606G
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sCVtIS_ATTANE-4606G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ATTANE™4606G ultra-low density polyethylene copolymer is used as the surface layer in the cast film, which has excellent low-temperature thermal adhesion properties, and has excellent tear strength and impact strength. In the processing of stretched films, ATTANE™4606G ultra-low density polyethylene copolymer has excellent stretchability, good physical properties and self-adhesive properties. ATTANE™4606G ultra-low density polyethylene copolymer can be used for co-extrusion processing of blown films. In this processing, ATTANE™4606G ultra-low density polyethylene copolymer is used as a heat seal layer in a multilayer film structure, and is co-extruded with other resins with excellent film bubble stability. Remarks: When unmodified is applied to the food contact field, ATTANE™4606G ultra-low density polyethylene copolymer meets the regulatory requirements for contact with food substances (FCN) under the U.S. Federal Food, Drug and Cosmetic Act, and its market access notice FCN 741 has been effective since September 28, 2007. The food contact certification notice allows the product to be used as an article or component in the production of articles in contact with food. These food types are described in the U.S. Food and Drug Administration Regulation 21 CFR § 176.170(c) Table -2 of the use conditions A to H. The composition of the product meets the regulatory requirements of EU Directive 2002/72/EC on food contact. Please contact your nearest Dow representative for proof of compliance with the Food Contact Act. Users remain responsible for determining whether the use of their products complies with all relevant regulations. Application field:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.911 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Puncture Energy (23 µm) | 2.80 | J | ASTM D5748 |
| Film Puncture Force (23 µm) | 35.0 | N | ASTM D5748 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm | 4.80 | MPa | ISO 527-3 |
| TD : Yield, 23 µm | 4.50 | MPa | ISO 527-3 |
| MD : Break, 23 µm | 28.0 | MPa | ISO 527-3 |
| TD : Break, 23 µm | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm | 450 | % | ISO 527-3 |
| TD : Break, 23 µm | 600 | % | ISO 527-3 |
| Dart Drop Impact (23 µm) | 180 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 23 µm | 200 | g | ASTM D1922 |
| TD : 23 µm | 360 | g | ASTM D1922 |
| Unstretched bond | 100 | g | ASTM D4649 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm) | 92 | ASTM D2457 | |
| Haze (23.0 µm) | 0.70 | % | ASTM D1003 |
| Additional Information |
|---|
| 对于在 Lab Collin 生产线上采用 15 米/分冷却辊于 25°C 下生产的单层薄膜所测量的薄膜属性。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 260 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜挤出的制造条件： 熔体温度：190 - 260 °C 建议的厚度范围：10 - 60 µm 脱离速度：150 - 300 米/分 冷却辊温度：20 - 60 °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA/ABS Blend 2010/2 UV | TER HELL PLASTIC GMBH | Nylon 6+ABS | TEREZ PA/ABS |
| ACLAR® 22A (2 mil) | Honeywell | PCTFE | ACLAR® |
| Adstif EA648P | LyondellBasell Industries | PP, High Crystal | Adstif |
| Cheng Yu FV30725 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| LNP™ THERMOCOMP™ AF004L compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
