Ultralast™ MC900
| Category: | PUR-Capro/MDI , Polyurethane (Polycaprolactone, MDI) |
| Manufacturer: | Chemtura |
| Trademark: | Ultralast™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sCTF0p_Ultralast-MC900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultralast Thermoplastic Urethanes combine our proprietary LF and polymerization technology that provide well-defined molecular structure, better phase segregation and stronger hard segments. Features of Ultralast MC900 include:
MARKETS Ultralast Thermoplastic Urethanes can meet the needs of diverse applications requiring performance. MC900 is designed but not limited to the recreational sports and industrial markets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 15 to 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.3 | % | |
| Across Flow : 24 hr | 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 89 to 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 28.5 | MPa | ASTM D790 |
| Abrasion Resistance - DIN | 16.0 | mm³ | DIN 53516 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Dynamic Properties | |||
| Storage Modulus : 30°C | 1.33E+8 | dynes/cm² | |
| Storage Modulus : 110°C | 6.30E+7 | dynes/cm² | |
| Tangent Delta : 30°C | 0.0440 | ||
| Tangent Delta : 110°C | 0.0530 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Trouser Tear Resistance | 78.3 | N/mm | ASTM D1938 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 7.52 | MPa | ASTM D412 |
| Tensile Strength | 30.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 570 | % | ASTM D412 |
| Tear Strength | ASTM D470 | ||
| Split 1 | 28 | kN/m | |
| Split | 30 | kN/m | |
| Compression Set (70°C, 22 hr) | 28 | % | ASTM D395B |
| Bayshore Resilience | 55 | % | ASTM D2632 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | -34.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 180 to 210 | °C | |
| Front Temperature | 180 to 210 | °C | |
| Nozzle Temperature | 180 to 210 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 20.0 to 55.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 to 195 | °C | |
| Cylinder Zone 3 Temp. | 175 to 195 | °C | |
| Cylinder Zone 5 Temp. | 175 to 195 | °C | |
| Melt Temperature | 190 to 220 | °C | |
| Die Temperature | 170 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Oil resistance, IRM #903 oil aged (3 weeks at 100°C) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo PP AZ564G | Sumitomo Chemical Asia | PP Copolymer | Sumitomo PP |
| Sylvin 9658-80UV Brown 7431 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AVALON® 60 ABX | Huntsman Corporation | TPU-Polyester | AVALON® |
| Latilub 66-01M G/50 | LATI S.p.A. | Nylon 66 | Latilub |
| TECHNYL® A 218G2 V50 BLACK 34N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |