ENVIROLOY® ENV15-NC390
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sC5DZG_ENVIROLOY-ENV15-NC390.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, Non-Halogenated - Non-Chlorinated Flame Retardant, UV Stabilized, w/Mold Release, Good Heat Resistance, RoHS Compliant NC390 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. Contact Enviroplas Regarding UL Recognized Versions Of This Product. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 240°C/5.0 kg | 16 | g/10 min | |
| 260°C/5.0 kg | 22 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2380 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.6 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | Internal Method | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 249 to 277 | °C | |
| Middle Temperature | 249 to 277 | °C | |
| Front Temperature | 254 to 288 | °C | |
| Nozzle Temperature | 249 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-764B | CHI MEI CORPORATION | ABS | POLYLAC® |
| Spartech Polycom SCR7-7006UR | Spartech Polycom | PC | Spartech |
| LNP™ LUBRICOMP™ WFL36 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| Sylvin 8225-80 White 1468 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® B 4239 000000 | LANXESS Corporation | PBT | POCAN® |