Lutene® LB5000
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sBvTwS_Lutene-LB5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LUTENE LB5000 is mainly intended for extrusion coating and can be processed uniform thickness and width. LUTENE LB5000 is also noted for the excellent heat stability and has good silicone coating processibility. LB5000 has a good adhesion strength with paper and paper board and excellent neck-in characteristic. LUTENE LB5000 contains no additives. Agency Ratings: USA FDA 21CRF 117.1520(c) Japaness Ministry of Health and Welfare Notification No. 20 Standard Applications: Flexible package (Tie layer or sealant layer of laminating film) Paper and paperboard coating (Release paper, paper cup, kraft paper) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 43 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 8.83 | MPa | |
| Break, Compression Molded | 11.8 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 550 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 196 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Seal Initiation Temperature 1 | 110 | °C | |
| Water Vapor Transmission | 20 | g/m²/24 hr | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 83.0 | °C | ASTM D1525 |
| Melting Temperature | 107 | °C | DSC |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion to Aluminum 2 | 392.3 | N/m | Internal Method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Minimum Coating Weight 3 | 13 | g/m² | Internal Method |
| Neck-in 4 | 20.0 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Kraft paper, 40 g/m² |
| 2 . | Coating weight: 40 g/m²(actually aluminum) |
| 3 . | Coating speed: 250 m/min |
| 4 . | Coating speed: 200 m/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-GP2-TFE5 | Polymer Resources Ltd. | PC | PRL |
| Trilliant™ HC THC-01-AS149031 Trans Blue | PolyOne Corporation | ABS | Trilliant™ HC |
| Elastollan® 670 AWHU | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| ELASTOSIL® LR 3066/40 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Sylvin 6252-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |