Horda E6756
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Horda Cable Compounds |
| Trademark: | Horda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sBT9vC_Horda-E6756.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
E6756 is an insulating, sheathing and jacketing material for low voltage energy cables. It offers good thermo mechanical properties and good surface finish. E6756 meets the requirements as below, when optimal processing extrusion and end testing procedure are used:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ASTM D1928 |
| Moisture 1 | ppm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 40.0 | °C | |
| Hopper Temperature | 23.0 | °C | |
| Cylinder Zone 1 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 2 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 3 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 4 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 5 Temp. | 60.0 - 110 | °C | |
| Die Temperature | 100 - 130 | °C |
| Extrusion instructions |
|---|
| Neck Temperature: 100 to 130°CHead Temperature: 100 to 130°C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 6000 A BK | POLY GIN | PC+ABS | MARCOBLEND |
| 4TECH® 9A22140 PS1 | 4Plas | Nylon 66 | 4TECH® |
| Capilene® Y 50 V | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| ColorRx® PP2-0900RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| Kazan LDPE 15313-003 OKP 22 1111 2003 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |