VALOX™ 430 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sAqoDf_VALOX-430-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33 % glass reinforced, impact modified. Connectors, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Specific Volume | 0.650 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.30 to 0.50 | % | |
| Flow 2 | 0.50 to 0.80 | % | |
| Flow : 3.20 mm | 0.50 | % | |
| Across Flow 3 | 0.40 to 0.60 | % | |
| Across Flow 4 | 0.60 to 0.90 | % | |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 5 | 8670 | MPa | ASTM D638 |
| Tensile Strength 6(Break) | 106 | MPa | ASTM D638 |
| Tensile Elongation 7(Break) | 3.1 | % | ASTM D638 |
| Flexural Modulus 8(50.0 mm Span) | 7810 | MPa | ASTM D790 |
| Flexural Strength 9(Break, 50.0 mm Span) | 174 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 860 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 223 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 208 | °C | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 10 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 2 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 1.5 to 3.2 mm |
| 2 . | 3.2 to 4.6 mm |
| 3 . | 1.5 to 3.2 mm |
| 4 . | 3.2-4.6 mm |
| 5 . | 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR H6 T/05 H XF V0 NATURAL 70 | PolyOne Corporation | PP Homopolymer | Maxxam™ FR |
| VITAMIDE® BX30WT6090 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| TORZEN® U4630HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Plaskon SMT-B-2HS | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| Deprene 203-40 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |