VITAMIDE® BT39NT6508
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s8K9ka_VITAMIDE-BT39NT6508.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® BT39NT6508 is a Polyamide 6 (Nylon 6) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| 24 hr | 1.3 | % | ASTM D570 |
| 23°C, 24 hr | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Break | 210 | MPa | ISO 527-2 |
| -- | 210 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 230 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 20.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | 95.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 95 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 215 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 220 | °C | ISO 1218, ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 30 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 550 | V | IEC 60112 |
| -- | 550 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® 775 CAF | Vyncolit N.V. | DAP | Vyncolit® |
| XYLEX™ X8303 resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| ALCOM® PA66 910/1.1 CF10 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| Hostalen PP H5416 | LyondellBasell Industries | PP Random Copolymer | Hostalen PP |
| IDI BMC B20 (Glass Content 8%) | IDI Composites International | TS, Unspecified | IDI BMC |