SABIC® PPcompound 37T1020
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s86WPx_SABIC-PPcompound-37T1020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 37T1020 is a high flow copolymer with 20% talc, offering an excellent balance between stiffness and impact resistance. It has been specially developed for automotive interior parts such as column cladding and door panels. SABIC® PPcompound 37T1020 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 28.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 25.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 45 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 6.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 18 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 3.0 | kJ/m² | |
| 0°C, Injection Molded | 3.5 | kJ/m² | |
| 23°C, Injection Molded | 5.7 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 8.0E-5 | cm/cm/°C | |
| 23 to 80°C | 1.1E-4 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk 40RNG30 | Shanghai Niuk New Plastic Technology Co., Ltd. | Nylon 6 | Niuk |
| En Chuan 6120TWA | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| Hanwha Total PP HY301 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |
| Kumho SSBR SOL-5150 | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| INNOPOL® PP CS 2-9110 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |