YUCLAIR® FN812
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s6bKMB_YUCLAIR-FN812.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
YUCLAIR FN812 is octene-1 copolymer designed for use in dry lamination film application. YUCLAIR FN812 provides stronger film than ones made from competitive LLDPE film grades. Therefore YUCLAIR FN812 shows superior tensile strength, tear strength, gel-free, antiblock and sealibility. YUCLAIR FN812 contains optimum of additives and is thus ideally suitable as a LLDPE resin for lamination film. YUCLAIR FN812 can be processed readily into blown film using standard extrusion techniques. YUCLAIR FN812 complies with FDA regulations in 21 CFR177.1520 for all food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | ASTM D746 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 11.8 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 10.8 | MPa | ASTM D882 |
| MD : Break, 50 µm | 53.9 | MPa | ASTM D882 |
| TD : Break, 50 µm | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 700 | % | ASTM D882 |
| TD : Break, 50 µm | 800 | % | ASTM D882 |
| Spencer Impact | 1.27 | J | ASTM D3420 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1922 | ||
| MD | 147.1 | kN/m | ASTM D1922 |
| TD | 196.1 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm) | 11 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Die Temperature | 190 - 195 | °C |
| Extrusion instructions |
|---|
| Film Extrusion Condition: Screw dia 50, Die dia 150, BUR 2.2Die gap 1.8, Screw RPM 45, L/S 7.2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR WC 0587-21 R2 RoHS | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| POLYMAN® (ABS) LP 340 | A. Schulman Europe | ABS | POLYMAN® |
| WPP PP PPC4TF1.3-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Andur 6 DPLM/Curene® 442 | Anderson Development Company | PUR-Ester/TDI | Andur |
| O'Tech OW 131 | O'Tech Corporation | PVC, Unspecified | O'Tech |