Desmopan® DP 89043D
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s6Dsvd_Desmopan-DP-89043D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| injection molding grade; no yellowing under the action of UV light; very good hydrolysis and microbial resistance; good low-temperature flexibility; high rebound resilience; low abrasion; colored applications in the automotive, sports and leisure sectors |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1080 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 95 | ||
| Shore D | 43 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2 | DIN 53504 | ||
| Break, 23°C | 30.0 | MPa | |
| 100% Strain, 23°C | 12.0 | MPa | |
| 300% Strain, 23°C | 18.0 | MPa | |
| Tensile Strain 3(Break, 23°C) | 700 | % | DIN 53504 |
| Flexural Modulus 4(23°C) | 80.0 | MPa | ISO 178 |
| Abrasion Resistance (23°C) | 11.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 230 | MPa | |
| 20°C | 143 | MPa | |
| 60°C | 101 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 56 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5(23°C) | 96 | kN/m | ISO 34-1 |
| Compression Set (70°C, 24 hr) | 41 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | 200 mm/min |
| 3 . | 200 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GF1750-N1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| LNP™ STAT-LOY™ K3000SZ compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-LOY™ |
| Luen Kee A-Grade | Luen Kee Plastic Materials Factory Limited | PC | Luen Kee |
| PERLEX® R2510 | A. Schulman Europe | PC | PERLEX® |
| Plenco 04504 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |