LNP™ THERMOCOMP™ RF00C compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s60eGz_LNPTHERMOCOMPRF00Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF00C is a compound based on Nylon 66 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound RF100-12 Product reorder name: RF00C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.30 - 0.50 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 234 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.3 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 17200 | MPa | ISO 178 |
| Flexural Stress | 349 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 75 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 262 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 254 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.9E-5 | cm/cm/°C | ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aegis® H95ZID | Honeywell | Nylon 6 | Aegis® |
| Baydur® 684 (15 pcf) | Covestro - PUR | PUR, Unspecified | Baydur® |
| ADENE ONOBG | A.D. Compound spa | PP Copolymer | ADENE |
| Formolene® 5102KR | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Osterlene® LLM1018SA | Osterman & Company | LLDPE | Osterlene® |