Dryflex® SE 40A201
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ELASTO |
| Trademark: | Dryflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s5qQFM_DryflexSE40A201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dryflex SE is our standard TPE range. It is extremely adaptable and can be used advantageously in many applications. The compounds are easy to process and are optimised for injection moulding. We have developed endless formulations to fulfil different properties and application requirements to optimise the finished component. Grades with improved compression set properties, high temperature resistance or more cost efficient values are an essential part of today's wide product spectrum. The Dryflex SE semi-filled series is recommended when the properties of the produced detail requires the advantages of the unfilled series in combination with the filled series. A semi-filled material can therefore combine the advantages of the other two series. The material has good flow and mechanical properties as well as reasonable scratch resistance. Compounds in the Dryflex SE semi-filled series are available in hardness from 30 to 90 Shore A in natural and black colours but they can easily be coloured. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 40 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow | ISO 37 | ||
| 100% strain | 0.900 | MPa | ISO 37 |
| 300% strain | 1.60 | MPa | ISO 37 |
| Tensile Stress - Across Flow (Break) | 7.70 | MPa | ISO 37 |
| Tensile Elongation - Across Flow (Break) | 900 | % | ISO 37 |
| Tear Strength 1 | 19 | kN/m | ISO 34-1 |
| Compression Set 2 | ISO 815 | ||
| 23°C, 72 hr | 17 | % | ISO 815 |
| 70°C, 22 hr | 35 | % | ISO 815 |
| 100°C, 22 hr | 62 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 200 - 220 | °C | |
| Mold Temperature | 15 - 50 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | C method: crescent sample |
| 2 . | Type B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 A | RTP Company | Nylon 6 | RTP |
| WELLAMID Nylon 6000 HWV0CP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| BIPEX B0620FN18 | Ginar Technology Co., LTD. | PBT | BIPEX |
| Hylon® N2000STL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Karina GRAY PVC COMPOUND 807D18/473-D-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |