Propafilm鈩?RGR03/120
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s5GG9g_Propafilm-RGR03-120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Release Film Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with surface polymers. RGR03/120 is part of a family of release films that are designed for use in a range of industrial applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow (129°C, 1 min) | 6.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.25 | ||
| vs. Itself - Static, Outside/Outside | 0.35 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3000 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 2300 | MPa | |
| 1% Secant, TD | 2100 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 210 | MPa | |
| TD : Yield | 170 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 80 | % | |
| TD : Break | 110 | % | |
| Yield | 36.7 | m²/kg | Internal Method |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 321T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| FRIANYL® A3 N V2 | Nilit Plastics | Nylon 66 | FRIANYL® |
| Loyblend® TA-1200 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| LUVOCOM® 20-8943 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| LUVOTECH® GS 46 | Lehmann & Voss & Co. | Nylon 46 | LUVOTECH® |