Order Products : sales@su-jiao.com
EVAL™ H171
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s3hdgZ_EVAL-H171.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
38 mol% Ethylene Vinyl Alcohol Copolymer H171B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.7 | g/10 min | |
| 210°C/2.16 kg | 3.4 | g/10 min | |
| Ethylene Content | 38.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 0.012 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 0.014 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.044 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 0.94 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 53.0 | °C | ISO 11357-2 |
| Melting Temperature | 172 | °C | ISO 11357 |
| Peak Crystallization Temperature | 148 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP RA12MN40 | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| Telcar® SGI85050 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Moplen EP 400H | LyondellBasell Industries | PP Copolymer | Moplen |
| Jam PE 52505 | Jam Petrochemical Company | HDPE | Jam PE |
| ISORENE™ AA7C1-1001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |