Polylink Power Cable P-10040-CB
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Polylink Polymers (India) Ltd. |
| Trademark: | Polylink Power Cable |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s3D3hN_Polylink-Power-Cable-P-10040-CB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
P-10040-CB is a defromation resistant semiconductive compound designed for use as shielding material both for conductior and insulation of power cable core. The compound is characterixed by its good stress crack resistance , balanced, volume, resistance,balanced volume resistivity and excellent proessability. APPLICATION : P-10040-CB is suitable as shielding material for cables up to 33 Kv. It is rated for 90deg.C continuous service and 130 deg.C overload temperature. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.91 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal) | > 100 | hr | IEC 60811 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 62.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Thermal shock- 4 hours. (130°C) | No flow / No crack | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+2 | ohms·cm | ASTM D257 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Cylinder Zone 1 Temp. | 130 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 150 | °C | |
| Cylinder Zone 4 Temp. | 160 | °C | |
| Adapter Temperature | 160 | °C | |
| Die Temperature | 160 | °C |
| Extrusion instructions |
|---|
| Screw cooling : 70°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 2002-4A | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Bergamid™ B65 G30 black IG | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Crastin® LW9020 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Fainplast PVC RE 140/1 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| LEXAN™ FST9436 resin | SABIC Innovative Plastics | PC | LEXAN™ |