FARBOSET® 2460
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Cosmic Plastics, Inc. |
| Trademark: | FARBOSET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s2hZvT_FARBOSET-2460.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Cosmic FARBOSET 2460 is a mineral-filled epoxy molding compound featuring fast cure rates, excellent moldability and superior thermal shock and moisture resistance. This compound was especially formulated for improved resistance to moisture ingress along with a high glass transition temperature for optimum reliability performance. It is designed to encapsulate a wide range of devices including tantalum and ceramic capacitors, resistors, resistor networks and high performance coils. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.88 | g/cm³ | |
| -- 1 | 2.14 | g/cm³ | |
| Apparent Density 2 | 1.00 | g/cm³ | |
| Spiral Flow | 79.0 | cm | |
| Molding Shrinkage - Flow | 0.40 | % |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | 55.2 | MPa | |
| Flexural Modulus | 13400 | MPa | |
| Flexural Strength | 89.6 | MPa | |
| Compressive Strength | 172 | MPa |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 165 | °C | |
| CLTE - Flow 3 | 4.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.8E+15 | ohms·cm | |
| Dielectric Strength (3.18 mm) | 14 | kV/mm | |
| Dielectric Constant | |||
| 60 Hz | 5.60 | ||
| 10 kHz | 5.40 | ||
| 1 MHz | 5.20 | ||
| Dissipation Factor | |||
| 60 Hz | 0.014 | ||
| 10 kHz | 0.018 | ||
| 1 MHz | 0.012 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.35 mm, Tested by Cosmic Plastics) | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life 4 | |||
| 4°C | 52 | wk | |
| 25°C | 1.0 | wk | |
| 35°C | 0.29 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time | |||
| 150°C 5 | 7.5E-3 | hr | |
| 150°C | 0.017 to 0.033 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 145 to 180 | °C | |
| Injection Pressure | 1.38 to 6.89 | MPa |
| Note Message | |
|---|---|
| 1 . | Molded |
| 2 . | Powder |
| 3 . | Alpha 1 |
| 4 . | Defined as not more than 40% loss of spiral flow based on original values. |
| 5 . | Hot Plate Cure Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyopt® LM11 | Suzhou OMAY Optical Materials Co., Ltd | Film, PMMA | Polyopt® |
| STRANOX PA6/45%LFT | Oxford Polymers | Nylon 6 | STRANOX |
| Nanjing Hongrui PC CS500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PC Alloy | Nanjing Hongrui PC |
| Di-Pak™ E-4501-5 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Duron PEI 2300 | ProPolymers Inc. | PEI | Duron |