INLUBE PPSLTF10
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INLUBE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s2Ag37_INLUBE-PPSLTF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% PTFE LUBRICATED, LINEAR POLYPHENYLENE SULFIDE |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 to 1.3 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 to 2.0 | % | ASTM D638 |
| Flexural Modulus | 3790 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 135 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 7.6E-3 to 0.013 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen 2000HEXP | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Borealis PP MD441U | Borealis AG | PP, Unspecified | Borealis PP |
| China PPS PTFE-hCF313 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| CYCOLOY™ C1200HF resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| Elastron® G G500.A30.N.PA | Elastron USA, Inc. | SEBS | Elastron® G |