GLS PC MG02
| Category: | PC , Polycarbonate |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s1KXX3_GLS-PC-MG02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC 10 GF Precolor |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 to 1.36 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | > 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 3300 | MPa | ASTM D638 |
| Tensile Strength 1(Yield) | > 60.0 | MPa | ASTM D638 |
| Flexural Modulus | > 3000 | MPa | ASTM D790 |
| Flexural Strength | > 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 135 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 85.0 to 122 | °C | |
| Injection Pressure | 68.0 to 104 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ1300 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| Telcar® TL-2555F | Teknor Apex Company | TPE | Telcar® |
| NEXT REGRIND PC/ABS MC8002-300RG | NEXT Specialty Resins, Inc. | PC+ABS | NEXT REGRIND |
| Fiberfil® J-60/30/E4 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Hostaform® C 9021 K | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |