NORYL GTX™ GTX902D resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s1GUFA_NORYLGTXGTX902Dresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL GTX GTX902D Resin is a blend of PPE/Polyamide 66. The material offers a unique pellet size compared to traditional NORYL GTX Resin. The material can be injection molded. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 3.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | ISO 527-2/50 |
| Fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 3 | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 160 | °C | ISO 306/B50 |
| -- | 162 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 270 - 300 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Minimum Moisture Content: .02 % |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8790-95UV Red 6229 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nylfor® A2 E2/2E NERO | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Durethan® B 30 S 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| Geon™ Vinyl Flexible EXPXV3910 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LUVOCOM® 1105-8592 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |