POLIMAXX 1111JXTA8
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | IRPC Public Company Limited |
| Trademark: | POLIMAXX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s19U4l_POLIMAXX-1111JXTA8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 1111JXTA8 is a PP Homopolymer with 40% talcum filler for injection molding process. It features medium melt flow, high flexural modulus and high heat resistance. It is suitable for auto parts and electrical appliances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 584 mm) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 36.3 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5880 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 53.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 2.94 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 147 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers Nylon 6604 HS | Network Polymers, Inc. | Nylon 66 | Network Polymers Nylon |
| Hyundai EP PA66 LD900 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| POLIMAXX 2311LCXTA6 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| KMI PP KM083-MJ | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| LEXAN™ 3412ECR resin | SABIC Innovative Plastics | PC | LEXAN™ |