Clariant Acetal HP-MF9
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Acetal |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s0wcny_Clariant-Acetal-HP-MF9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clariant Acetal HP-MF9 is an Acetal (POM) Homopolymer material. It is available in North America for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 166 | °C | |
| 1.8 MPa, Unannealed | 130 | °C | |
| Melting Temperature | 177 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 171 to 182 | °C | |
| Middle Temperature | 185 to 193 | °C | |
| Front Temperature | 196 to 202 | °C | |
| Nozzle Temperature | 204 to 218 | °C | |
| Mold Temperature | 60.0 to 90.6 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.00 to 10.3 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 280 H | RTP Company | Nylon 66 | RTP |
| Bergamid™ BG6000-8034 RS NC001 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Argothane® D7101 | Argotec LLC | TPU, Unspecified | Argothane® |
| Leona™ 93G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Axiall PVC 1701 | Axiall Corporation | PVC, Flexible | Axiall PVC |