Order Products : sales@su-jiao.com
Hostacom HYG 343L 356015
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s0oYkg_HostacomHYG343L356015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom HYG 343L 356015 is a 40% glass fiber reinforced PP homopolymer, with very high melt flow rate, very good color stability in hot water or steam, very good hot water resistance, very high stiffness and excellent LTHS (long term heat stability). Product is UL listed. Please contact Lyondellbasell for shrinkage recommendations. Relative temperature index Mech w/Imp. The product is also available as a customized color matched, pellet form. This grade is delivered in 356015 color version. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.25 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 26 - 36 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 25.0 - 35.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 114 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 2.2 | % | ISO 527-2 |
| Fracture | 2.5 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 9200 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 47 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.0 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® 8407APUV | Poliolefinas Internacionales, C.A. (Polinter) | MDPE | VENELENE® |
| VENYL SN002 - 7847 | AD majoris | Nylon 6 | VENYL |
| Yanshan PE 6600B | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| CP PRYME® Nylon 6 N100MD2 | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Ultramid® A3WG7 HR BK23591 | BASF Corporation | Nylon 66 | Ultramid® |