ENGAGE™ HM 7289
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | s0RGeb_ENGAGE-HM-7289.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ENGAGE™ HM 7289 Polyolefin Elastomer Resin is a unique olefinic composition for improved processability and material handling. This product is produced via gas phase polymerization from Dow. This is an ethylene-butene copolymer exhibiting high flexibility, elasticity, and high melt strength for film and extruded sheet applications. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.891 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | < 0.50 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 150°C) | 74 | MU | ASTM D1646 |
| Total Crystallinity - % | 27.5 | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| 1.00 mm, Extruded 1 | 88 | ||
| Shore A, Compression Molded | 88 | ||
| Shore D, Compression Molded | 31 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 2(Compression Molded) | 2.80 | MPa | ASTM D638 |
| Tensile Strength 3(Break, Compression Molded) | 3.70 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, Compression Molded) | 200 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 49.1 | MPa | |
| 2% Secant : Compression Molded | 43.5 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| Across Flow : Break, 1.00 mm | 14.1 | MPa | |
| Flow : Break, 1.00 mm | 20.6 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Across Flow : Break, 1.00 mm | 650 | % | |
| Flow : Break, 1.00 mm | 670 | % | |
| Tear Strength 5 | ASTM D624 | ||
| -- 6 | 56.6 | kN/m | |
| Across Flow : 1.00 mm 7 | 65.0 | kN/m | |
| Flow : 1.00 mm 8 | 68.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.2 | °C | Internal Method |
| Vicat Softening Temperature | 53.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 9 | 98.9 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | Extruded sheet |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | 510 mm/min |
| 5 . | Die C |
| 6 . | Compression Molded |
| 7 . | Extruded sheet |
| 8 . | Extruded sheet |
| 9 . | 10°C/min, Dow method, complete protocols available upon request. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EPLON 66 GFR 30 BK | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLON 66 |
| InnoPlus HD8200B | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Jam PE 16503 | Jam Petrochemical Company | LLDPE | Jam PE |
| Lifoflex® UV 40 GA 1040 | ELASTO | SEBS | Lifoflex® |
| Plenco 04304 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |