EXTEM™ VH1003F resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | EXTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rzui5Q_EXTEM-VH1003F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, Thermoplastic Polyimide (TPI) resin. Glass transition Temp. (Tg) of 247°C. Global Food Contact Approval. Resin is subject to Commerce Control Laws U.S. 15CFR Chapter VII, Part 774 and Annex I of Reg. EC 428/2009 as ECCN1C008. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (367°C/6.6 kg) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 8.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.8 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 141 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3520 | MPa | ASTM D638 |
| -- | 3120 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 96.5 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2/5 |
| Break 4 | 96.5 | MPa | ASTM D638 |
| Break | 78.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 6.0 | % | ASTM D638 |
| Yield | 8.5 | % | ISO 527-2/5 |
| Break 6 | 50 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 3170 | MPa | ASTM D790 |
| -- 8 | 3080 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 123 | MPa | ISO 178 |
| Yield, 100 mm Span 9 | 155 | MPa | ASTM D790 |
| Break, 50.0 mm Span 10 | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 11 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 74 | J/m | ASTM D256 |
| 23°C | 69 | J/m | ASTM D256 |
| -30°C 12 | 5.4 | kJ/m² | ISO 180/1A |
| 23°C 13 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| -30°C 14 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 33.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 237 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 217 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 230 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 15 | 228 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 242 | °C | ASTM D1525, ISO 306/B50 12 16 |
| -- | 238 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 3.41 | ||
| 1 kHz | 3.41 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.025 | ||
| 60 Hz | 0.025 | ||
| 100 Hz | 8.0E-3 | ||
| 1 kHz | 1.0E-3 | ||
| 1 MHz | 7.0E-3 | ||
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 45 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 58.0 | % | ASTM D1003 |
| Haze (2540 µm) | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 360 to 382 | °C | |
| Middle Temperature | 371 to 393 | °C | |
| Front Temperature | 382 to 404 | °C | |
| Nozzle Temperature | 377 to 399 | °C | |
| Processing (Melt) Temp | 382 to 404 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 2.6 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| 16 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202 FR | RTP Company | Nylon 66 | RTP |
| RTP 103 HI UV | RTP Company | PP, Unspecified | RTP |
| Sindustris ABS LXR510E | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TRIMID® N66-1010 | Polymer Technology and Services, LLC | Nylon 66 | TRIMID® |
| NORYL™ PKN4752 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |