Edgetek™ PC-20GF/000 MR BLACK
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rzZOPY_Edgetek-PC-20GF-000-MR-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fiber reinforced polycarbonate compound with outstanding mold releasing property |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage (3.00 mm) | 0.10 - 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 110 | MPa | ASTM D638 |
| Flexural Modulus 2 | 5800 | MPa | ASTM D790 |
| Flexural Strength 3 | 150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 138 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 280 - 310 | °C | |
| Middle Temperature | 280 - 310 | °C | |
| Front Temperature | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P IR H-50 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| Torayca® 3101T-10V | Toray Resin Company | Nylon 66 | Torayca® |
| Tuftec™ H1053 | AKelastomers | SEBS | Tuftec™ |
| Clyrell RC1908 | LyondellBasell Industries | PP Copolymer | Clyrell |
| PHOENIX™ 16601 | Phon Tech Industrial Company | TPV | PHOENIX™ |