LNP™ THERMOCOMP™ SF00A compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rx9AMB_LNP-THERMOCOMP-SF00A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP SF00A is a compound based on Nylon 12 resin containing 50% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound SF-100-10 Product reorder name: SF00A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12800 | MPa | ASTM D638 |
| -- | 12300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 121 | MPa | ASTM D638 |
| Yield | 113 | MPa | ISO 527-2/5 |
| Break 3 | 121 | MPa | ASTM D638 |
| Break | 113 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.8 | % | ASTM D638 |
| Yield | 1.5 | % | ISO 527-2/5 |
| Break 5 | 1.8 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 8930 | MPa | ASTM D790 |
| -- 7 | 11.0 | MPa | ISO 178 |
| Flexural Strength 8 | ASTM D790 | ||
| Yield, 50.0 mm Span | 148 | MPa | |
| Break, 50.0 mm Span | 143 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 97 | J/m | ASTM D256 |
| 23°C 9 | 1.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 10 | 31 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 16.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 176 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 166 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 176 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 216 to 227 | °C | |
| Middle Temperature | 221 to 232 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTAMID™ MA3EG8 | Marplex Australia Pty. Ltd. | Nylon 66 | ASTAMID™ |
| Durethan® BKV 25 F30 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| KumhoSunny PC/ABS HAC8250NH-DF10 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| LOXIM 210 01 HB | LOXIM Industries Private Limited | PBT | LOXIM |
| ESTOPLAST XU 6730NN93 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |