DOWLEX™ 2006G
| Category: | HDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rwWRf9_DOWLEX-2006G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dowlex™ 2006G Polyethylene Resin is an ethylene 1-octene copolymer, suitable for cast film applications and also perfectly designed to give excellent filler acceptance and low torque during compounding. Dowlex™ 2006G offers superior stiffness and excellent temperature resistance making it the perfect partner for down gauging. Films produced using Dowlex™ 2006G offer low shrinkage which is ideal when registered printing is used. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 38.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 19.0 | MPa | ASTM D882 |
| MD : 20 µm 1 | 21.0 | MPa | ASTM D882 |
| TD : 20 µm 2 | 15.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 700 | % | ASTM D882 |
| TD : Break, 20 µm | 15 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 29 | g | ASTM D1922 |
| TD : 20 µm | 390 | g | ASTM D1922 |
| Extrusion instructions |
|---|
| Cast film extrusion conditions: Melt Temperature: 220°C Die gap: 0.7 mm Film thickness: 20 microns |
| Note Message | |
|---|---|
| 1 . | @ 5% Elongation |
| 2 . | @ 5% Elongation |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp DBS5906 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Aurora PVC AP2254 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Karina BLACK PVC COMPOUND 90901-48/1-D-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lumid® HI5001AS | LG Chem Ltd. | Nylon+Olefin | Lumid® |
| POLYFORT® FPP 1220 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |