XYRON™ DG141
| Category: | PPS+PPE , Polyphenylene Sulfide + PPE |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rwORvc_XYRON-DG141.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE PPS/PPE alloy 40% Filler reinforced Flame retardant V-0 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 0.10 to 0.40 | % | Internal Method |
| Outdoor Suitability (Black) | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 89.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 147 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 4.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 241 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength 3(2.00 mm) | 27 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 4.10 | ||
| 1 MHz | 4.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 2.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 300 to 330 | °C | |
| Mold Temperature | 90.0 to 130 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x2 mm |
| 2 . | 4 mm |
| 3 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT 5003P1 | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| Vibrathane® B895 | Chemtura | PUR-Ether/MDI | Vibrathane® |
| DOMAMID® 66G30V0AH | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| HIPOLEN P® GM 31 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| PENTAMID B GV40 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |