RTP 143 HI MF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rwMYPX_RTP-143-HI-MF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.6 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1720 | MPa | ASTM D638 |
| Tensile Strength | 21.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 10 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Flexural Strength | 34.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 107 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 66.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Molding Shrinkage, Linear-Flow, ASTM D955, 6.35mm: 20mm/m. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 - 260 | °C | |
| Middle Temperature | 204 - 260 | °C | |
| Front Temperature | 204 - 260 | °C | |
| Mold Temperature | 24.0 - 52.0 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Surlyn® 9945 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| TAROMID A 280 G6 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| LNP™ STAT-KON™ FD000 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ STAT-KON™ |
| Plexiglas® LED white 0V200 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Akulon® FC-X9200 | DSM Engineering Plastics | Nylon 6 | Akulon® |