SURPASS® RMs341-U(UG)

Category:	HDPE , High Density Polyethylene
Manufacturer:	NOVA Chemicals
Trademark:	SURPASS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rukKSs_SURPASS-RMs341-U-UG-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

SURPASS® RMs341-U(UG) is a High Density Polyethylene material. It is available in North America for rotational molding.

Important attributes of SURPASS® RMs341-U(UG) are:

Flame Rated

Antioxidant

Fast Molding Cycle

Good Mold Release

Good Processability

Typical applications include:

Plumbing/Piping/Potable Water

Food Contact Applications

Tanks

Containers

Sporting Goods

General Information
Additive	Antioxidant UV Stabilizer
Features	Antioxidant Fast Molding Cycle Good Mold Release Good Processability High Density Low Temperature Impact Resistance Low Viscosity Octene Comonomer
Uses	Containers Septic Tanks Sporting Goods Tanks
Agency Ratings	FDA 21 CFR 176.170(c), Table 2 3 FDA 21 CFR 177.1520(c) 3.2a 4 NSF 24 NSF 51 NSF 61
Processing Method	Rotational Molding

Physical	Nominal Value	Unit	Test Method
Density	0.941	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	3.5	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
50°C, 100% Igepal, Compression Molded, F50	> 1000	hr	ASTM D1693A
50°C, 100% Igepal, Compression Molded, F50	> 1000	hr	ASTM D1693B

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, 1.90 mm, Compression Molded)	20.2	MPa	ASTM D638
Tensile Elongation ²(Yield, 1.90 mm, Compression Molded)	12	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	827	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
ARM Impact - Rotational Molded			ARM
-40°C, 3.17 mm	95.0	J
-40°C, 6.35 mm	230	J

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed, Compression Molded	62.0	°C
1.8 MPa, Unannealed, Compression Molded	43.0	°C
Melting Temperature	126	°C	DSC

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Note Message
1 .	Type IV, 51 mm/min
2 .	Type IV, 51 mm/min

Resin Grade	Manufacturer	Category	Trademark
RTP 1501-72D	RTP Company	TPE	RTP
Next PC CXF-01NC	Next Polymers Ltd.	PC	Next PC
FLEXCHEM™ 3551-02	Colorite Polymers	PVC, Flexible	FLEXCHEM™
LEXAN™ FXEMPX2L resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™
LEXAN™ EXL9414T resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™