AMPLIFY™ TY 2551
| Category: | MAH-g , Functional Polymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AMPLIFY™ TY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ruNaye_AMPLIFY-TY-2551.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AMPLIFY TY 2551 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 2551 Functional Polymer promotes adhesion of polypropylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH) and other polar substrates. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.896 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| MAH Graft Level 1 | Low | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 23.0 | MPa | ASTM D638 |
| Fracture | 17.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 758 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 7.03 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 758 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 703 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 27.7 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 25.0 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 34.5 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 22.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 630 | % | ASTM D882 |
| TD : Fracture, 51 µm | 520 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 100 | g | ASTM D1709A |
| Elmendorf Tear Strength 2 | ASTM D1922 | ||
| MD : 51 µm | 20 | g | ASTM D1922 |
| TD : 51 µm | 40 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 148 | °C | ASTM D4591 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 35 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 - 238 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 2.5 in. (63.5 mm); 24:1 L/D Screw Type: Barrier screw Die Gap: 70 mil (1.8 mm) Melt Temperature: 450 °F Output: 6 lb/hr/in. of die circumference Die Diameter: 6 in. Blow-Up Ratio: 2.5:1 Screw Speed: 70 rpm |
| Note Message | |
|---|---|
| 1 . | Low: <0.25 wt%, Medium 0.25-0.5, High >0.5 wt% |
| 2 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3400 G-930 | RTP Company | LCP | RTP |
| EVALENE® PP PHJ1201 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| LEXAN™ 4501 resin | SABIC Innovative Plastics | PPC | LEXAN™ |
| LNP™ THERMOCOMP™ Noryl_HM4025 compound | SABIC Innovative Plastics | PPE+PS | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ RF006XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |