RAMOFIN PPH308G6
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rthGqC_RAMOFIN-PPH308G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS-FIBER REINFORCED, HEAT STABILIZED, IMPACT MODIFIED POLYPROPYLENE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.10 - 0.40 | % | ASTM D955 |
| -- | 0.10 - 0.40 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 115 | ASTM D785 | |
| R scale | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 95.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5900 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 115 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 75 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C | 14 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 153 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 145 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 140 | °C | |
| Maximum Continuous Use Temperature | 110 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 40 | mm/min | FMVSS 302 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 225 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA66 A 2050/100 GF50 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Flontech® FT-GL15-M3-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| ELIX™ ABS M205FC | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Geon™ Vinyl Wire & Cable W2403L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| KOPLA PP KPT1040 | KOPLA Co., Ltd. | PP, Unspecified | KOPLA PP |