4PET® 9L22120 H
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | 4Plas |
| Trademark: | 4PET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rtaQ9n_4PET-9L22120-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PET 9L22120 H is a Standard Flow 20% Glass Fibre Reinforced Heat Stabilised PET |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (270°C/2.16 kg) | 45 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction | 1.0 | % | |
| Flow direction | 0.30 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 1000 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 25 | kJ/m² | ISO 180/1U |
| 23°C | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B |
| Melting Temperature 2 | 250 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 90.0 - 140 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Polyethylene F320 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| China PPS hMR60 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Lion Idemitsu Composites PPS C-21OSF | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| MACOMASS PVC MM-PVC I 1560 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |
| LNP™ THERMOCOMP™ EC006 compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |