Generic PC - Carbon Powder
| Category: | PC , Polycarbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rtWYrG_Generic-PC---Carbon-Powder.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC - Carbon Powder This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 - 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.39 - 0.81 | % | ASTM D955 |
| Transverse flow : 23°C | 0.40 - 0.82 | % | ASTM D955 |
| 23°C | 0.39 - 0.84 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.098 - 0.18 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.14 - 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2480 - 3460 | MPa | ASTM D638 |
| 23°C | 2580 - 3750 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 59.8 - 67.7 | MPa | ASTM D638 |
| Yield, 23°C | 55.0 - 64.2 | MPa | ISO 527-2 |
| Fracture, 23°C | 49.8 - 64.6 | MPa | ASTM D638 |
| Fracture, 23°C | 53.4 - 64.6 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.2 - 4.9 | % | ASTM D638 |
| Yield, 23°C | 4.1 - 4.6 | % | ISO 527-2 |
| Fracture, 23°C | 3.7 - 11 | % | ASTM D638 |
| Fracture, 23°C | 3.2 - 13 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2710 - 3530 | MPa | ASTM D790 |
| 23°C | 2480 - 3520 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 96.4 - 117 | MPa | ASTM D790 |
| 23°C | 102 - 109 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 23 - 120 | J/m | ASTM D256 |
| 23°C | 2.4 - 9.7 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 510 - 2400 | J/m | ASTM D256 |
| 23°C | 37 - 140 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 1.93 - 39.4 | J | ASTM D3763 |
| 23°C | 0.700 - 36.1 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 86.7 - 142 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 88.4 - 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 82.2 - 134 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.0 - 132 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | |||
| Flow | 5.2E-5 - 6.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral | 5.2E-5 - 6.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 5.2E-5 - 5.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0 - 1.3E+10 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 121 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.025 | % | |
| Rear Temperature | 254 - 299 | °C | |
| Middle Temperature | 260 - 316 | °C | |
| Front Temperature | 266 - 327 | °C | |
| Processing (Melt) Temp | 271 - 316 | °C | |
| Mold Temperature | 51.7 - 96.7 | °C | |
| Back Pressure | 0.258 - 0.265 | MPa | |
| Screw Speed | 45 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC - Carbon PowderThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® M-601 | Matrix Polymers | PE, Unspecified | REVOLVE® |
| DILAMID® 6 NATURAL | Dilaplast S.p.A. | Nylon 6 | DILAMID® |
| ISOTHANE® 1170D | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| Piolen® P T40A37 | PiO Kunststoffe GmbH & Co KG | PP Copolymer | Piolen® P |
| Sylvin 4225-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |