Reny® 1722F
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rtTOAQ_Reny-1722F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® 1722F is a Polyarylamide (PARA) material filled with 50% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1722F: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.65 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 20 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 12.5 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.48 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.13 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.70 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20700 | 19100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 244 | 208 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 1.7 | % | ISO 527-2 |
| Flexural Modulus | 18900 | 18800 | MPa | ISO 178 |
| Flexural Stress | 381 | 319 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 58 | 54 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 237 | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 226 | 219 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 LS | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| WELLAMID Nylon 6000 CF 18 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ALFATER XL® D40E 1GP0010 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| AVALON® 70 ABX | Huntsman Corporation | TPU-Polyester | AVALON® |
| LNP™ THERMOCOMP™ RF008XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |