Raditer® B RV200
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Radici Plastics |
| Trademark: | Raditer® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rqCteG_Raditer-B-RV200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT 20% Glass Fiber reinforced injection moulding grade. Enhanced stiffness and dimensional stability. Natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/eA | ||
| -30°C | 5.3 | kJ/m² | ISO 179/eA |
| 23°C | 5.9 | kJ/m² | ISO 179/eA |
| Charpy Unnotched Impact Strength | ISO 179/eU | ||
| -30°C | 29 | kJ/m² | ISO 179/eU |
| 23°C | 32 | kJ/m² | ISO 179/eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 210 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 195 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357-1-3 at a heating rate of 10°C/min. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POYAD CR207I | Pooya Polymer Tehran | PE, Unspecified | POYAD |
| SEPAZ™ LB50 | Mando Advanced Materials Co., Ltd. | Nylon 6 | SEPAZ™ |
| SUPREME GPPS SC205 | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Kelon® A FR H2 CETG/300-V0 | LATI S.p.A. | Nylon 66 | Kelon® A |
| Ipethene® 322 | Carmel Olefins Ltd. | LDPE | Ipethene® |