Tenac™ 5013A
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rp1B3S_Tenac-5013A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ 5013A is an Acetal (POM) Homopolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ 5013A include engineering/industrial parts, automotive and housings. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 to 2.2 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 94 | ||
| R-Scale | 120 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 71.0 | MPa | ISO 527-2 |
| -- | 69.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 2950 | MPa | ASTM D790 |
| -- | 2900 | MPa | ISO 178 |
| Flexural Strength | 101 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 13.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 164 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 102 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 to 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 to 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Arc Resistance | 250 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ 2410R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| ADENE GHFAG | A.D. Compound spa | PP Copolymer | ADENE |
| GS Pla® AZ91T | Mitsubishi Chemical Performance Polymers, Inc. | Biodeg Polymers | GS Pla® |
| LEXAN™ LC120 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| OnFlex™ S KE 70A-3S1726 | PolyOne Corporation | TPE | OnFlex™ |