Sinkral® PD L 322
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Sinkral® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rmfD5G_Sinkral-PD-L-322.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sinkral PD L 322 by continuous Mass, is a general purpose, high flow injection molding grade having good impact resistance coupled with an excellent gloss. Designation: Thermoplastic ISO 2580-ABS 1,MG,095-25-16-25 Widely used in the small and large household appliance sector, vacuum cleaners, toys, telephones and consumer electronics. Grade available in natural color only. The composition of this grade meets European Regulations for packaging in contact with foodstuffs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 20 | % | ASTM D638 |
| Flexural Modulus 3 | 2350 | MPa | ASTM D790 |
| Flexural Strength 4 | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | DIN 53453 |
| Charpy Unnotched Impact Strength | DIN 53453 | ||
| -40°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -40°C, 3.20 mm | 50 | J/m | ISO 180/4A |
| -20°C, 3.20 mm | 70 | J/m | ISO 180/4A |
| 0°C, 3.20 mm | 100 | J/m | ISO 180/4A |
| 23°C, 3.20 mm | 170 | J/m | ISO 180/4A |
| -40°C 5 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 6 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 96.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ISO 306/A120 |
| -- | 96.0 | °C | ISO 306/B120 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.17 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 kHz) | 3.10 | IEC 60250 | |
| Dissipation Factor (1 kHz) | 0.015 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | Internal Method | |
| Glow Wire Ignition Temperature (3.00 mm) | 650 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Designation | Thermoplastic ISO 2580-ABS 1,MG,095-25-16-25 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 4 mm |
| 6 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multilon® DN-7730M | TEIJIN LIMITED | PC+ABS | Multilon® |
| LUVOCOM® 65-8570/BL | Lehmann & Voss & Co. | PP Copolymer | LUVOCOM® |
| Osterlene® PPC-57-1.4-N | Osterman & Company | PP Impact Copolymer | Osterlene® |
| TECHNYL® A 718 V30 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| NORYL™ WCD835 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |