Durethan® BKV 30 XTS1 901510

Category: Nylon 6 , Polyamide 6
Manufacturer: LANXESS GmbH
Trademark: Durethan®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: rmWWeA_DurethanBKV30XTS1901510.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
PA 6, 30 % glass fibers, injection molding, heat-aging stabilized, notably high heat-aging stability
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 30% filler by weight
Additive
  • heat stabilizer
Features
  • Good heat aging resistance
  • Heat resistance, high
  • Thermal Stability
Processing Method
  • Injection molding
PhysicalDryConditionedUnitTest Method
Density (23°C)1.36--g/cm³ISO 1183
Apparent Density 0.70--g/cm³ISO 60
Molding Shrinkage ISO 2577
     Vertical flow direction : 280°C, 2.00mm 10.63--%ISO 2577
     Vertical flow direction : 120°C, 4 hours, 2.00mm 20.14--%ISO 2577
     Flow direction : 280°C, 2.00mm 30.25--%ISO 2577
     Flow direction : 120°C, 4 hours, 2.00mm 40.050--%ISO 2577
MechanicalDryConditionedUnitTest Method
Tensile Modulus (23°C)95005300MPaISO 527-2/1
Tensile Stress (Break, 23°C)17085.0MPaISO 527-2/5
Tensile Strain (Break, 23°C)3.06.0%ISO 527-2/5
Nominal Tensile Strain at Break (23°C)3.05.5%ISO 527-2/50
Flexural Modulus 5(23°C)94005200MPaISO 178/A
Flexural Stress ISO 178/A
     3.5% strain, 23°C --120MPaISO 178/A
     23°C 6250140MPaISO 178/A
Flexural Strain at Flexural Strength 7(23°C)3.05.0%ISO 178/A
Additional InformationDryConditionedTest Method
ISO Shortname PA 6, GHR, 14-100, GF30--ISO 1874
InjectionDryUnitTest Method
Residual Moisture Content 0.030 - 0.12%Karl Fisher
ImpactDryConditionedUnitTest Method
Charpy Notched Impact Strength ISO 179/1eA
     -30°C 9.0--kJ/m²ISO 179/1eA
     23°C 10--kJ/m²ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)60--kJ/m²ISO 179/1eU
Notched Izod Impact ISO 180/1A
     -30°C 9.0--kJ/m²ISO 180/1A
     23°C 1015kJ/m²ISO 180/1A
Unnotched Izod Impact Strength (23°C)5070kJ/m²ISO 180/1U
ThermalDryConditionedUnitTest Method
Heat Deflection Temperature
     0.45 MPa, not annealed 215--°CISO 75-2/B
     1.8 MPa, not annealed 200--°CISO 75-2/A
Melting Temperature 8221--°CISO 11357-3
Linear thermal expansion coefficient ISO 11359-2
     Flow : 23 to 55°C 1.9E-5--cm/cm/°CISO 11359-2
     Lateral : 23 to 55°C 1.1E-4--cm/cm/°CISO 11359-2
InjectionDryUnitTest Method
Drying Temperature - Dry Air Dryer 80.0°C
Drying Time - Dry Air Dryer 2.0 - 6.0hr
Processing (Melt) Temp 250 - 290°C
Mold Temperature 80.0 - 100°C
Note Message
1 .60x60x2mm, 80°C MT, 600 bar
2 .60x60x2mm
3 .60x60x2mm, 80°C MT, 600 bar
4 .60x60x2mm
5 .2.0 mm/min
6 .2.0 mm/min
7 .2 mm/min
8 .10°C/min
Resin Grade Manufacturer Category Trademark
Primefin V525MI25UV Lucent Polymers, Inc. PP, Unspecified Primefin
Evermore PUR SC-636HR Evermore Chemical Industry Co., Ltd. PUR, Unspecified Evermore PUR
GERMAMID 6.6 FE 60 Kunststoff-Kontor-Hamburg GmbH Nylon 66 GERMAMID
LEXAN™ 101R resin SABIC Innovative Plastics Europe PC LEXAN™
Karina ORANGE PVC COMPOUND 920D32/ 91 Karina Ind. e Com. de Plásticos Ltda PVC, Unspecified Karina