RAMLLOY PBB104
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMLLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rmB9SE_RAMLLOY-PBB104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS ALLOY FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 260°C/5.0 kg | 30 | g/10 min | ASTM D1238 |
| 300°C/1.2 kg | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.70 | % | |
| -- | 0.40 - 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | > 30 | % | ASTM D638, ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 500 | J/m | ASTM D256 |
| 23°C | 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 120 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 100 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 116 | °C | ASTM D1525, ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 240 - 250 | °C | |
| Front Temperature | 250 - 265 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Pressure | 70.0 - 100 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/secMax Circumfrential Speed: 0.3 m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV HI K1416 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Toyolac® 450Y X10 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| XANTAR® C CM 206 U | Mitsubishi Engineering-Plastics Corp | PC+ABS | XANTAR® C |
| FHR Polypropylene 44S2A | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| LEXAN™ 500R resin | SABIC Innovative Plastics | PC | LEXAN™ |