SOLARENE F654
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Dongbu Hannong Chemical |
| Trademark: | SOLARENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rlTuW5_SOLARENE-F654.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLARENE F654 is a General Purpose Polystyrene product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 65 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 28.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638 |
| Flexural Modulus | 1960 | MPa | ASTM D790 |
| Flexural Strength | 42.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 76.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 93.0 | °C | ASTM D1525 1 |
| -- | 81.0 | °C | ASTM D1525 2 |
| RTI Elec | UL 746 | ||
| 1.59 mm | 50.0 | °C | |
| 3.17 mm | 50.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.59 mm | 50.0 | °C | |
| 3.17 mm | 50.0 | °C | |
| RTI Str | UL 746 | ||
| 1.59 mm | 50.0 | °C | |
| 3.17 mm | 50.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.50 | ASTM D150 | |
| Arc Resistance | ASTM D495 | ||
| 1.59 mm | PLC 7 | ||
| 3.17 mm | PLC 7 | ||
| Comparative Tracking Index (CTI) | UL 746 | ||
| 1.59 mm | PLC 2 | ||
| 3.17 mm | PLC 2 | ||
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.59 mm | PLC 4 | ||
| 3.17 mm | PLC 3 | ||
| High Voltage Arc Tracking Rate (HVTR) | UL 746 | ||
| 1.59 mm | PLC 2 | ||
| 3.17 mm | PLC 2 | ||
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.59 mm | PLC 4 | ||
| 3.17 mm | PLC 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm, ALL | V-2 | ||
| 3.17 mm, ALL | V-2 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2452L | Teknor Apex Company | TPE | Telcar® |
| CAPROWAX P™ 6006-11-000 Granulat | POLYFEA | Biodeg Polymers | CAPROWAX P™ |
| Generic PC+Polyester - Glass Fiber | Generic | PC+Polyester | Generic |
| Kimura® K2CD | Precision Polymer Engineering Ltd. | Elastomer, Specialty | Kimura® |
| ESTOPLAST EP 1115-N | Ester Industries Ltd. | PBT | ESTOPLAST EP |