NYLAFORCE® dynamic B 50
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LEIS Polytechnik - polymere Werkstoffe GmbH |
| Trademark: | NYLAFORCE® dynamic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | riHNds_NYLAFORCE-dynamic-B-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| produced by feed up-process, polyamide 6 + 50% glass fibres, heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.10 to 0.50 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C 2 | -- | 12500 | MPa | |
| 23°C | 18000 | -- | MPa | |
| Tensile Stress | ISO 527-2 | |||
| 23°C 3 | -- | 175 | MPa | |
| 23°C | 270 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, 23°C 4 | -- | 5.5 | % | |
| Break, 23°C | 3.3 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -- | 18 | -- | kJ/m² | |
| 23°C 5 | -- | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -- | No Break | -- | ||
| 23°C 6 | -- | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 221 | -- | °C | ISO 3146 |
| Note Message | |
|---|---|
| 1 . | 60 mm x 60 mm x 2 mm |
| 2 . | Tested according to ISO 527/ISO 1110 |
| 3 . | Tested according to ISO 527/ISO 1110 |
| 4 . | Tested according to ISO 527/ISO 1110 |
| 5 . | Testing according to ISO 179/ISO 1110 |
| 6 . | Testing according to ISO 179/ISO 1110 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP5007 | PolyMirae | PP Random Copolymer | Moplen |
| Badamid® PA12 GK30 | Bada AG | Nylon 12 | Badamid® |
| FRAGOM PR/04 AFKK | Crosspolimeri S.p.A. | TP, Unspecified | FRAGOM |
| KEBAFLEX® SG 25 A.1 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| OTECH PVC OW1065 - Wire Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |